PRODUCT STANDARD AND SIZE
| Size OD | Tolerance OD | Tolerance WT |
| ≤1/2″(≤12.7 mm) | ±0.005″(±0.13 mm) | ±15% |
| 1/2″<OD≤1″(12.7<OD≤25.4 mm) | ±0.005″(±0.13 mm) | ±10% |
CHEMICAL COMPOSITION
| C | Mn | P | S | Si | Cr | Ni | Mo | N | Cu |
| % | % | % | % | % | % | % | % | % | % |
| Max | Max | Max | Max | Max | Max | Max | |||
| 0.030 | 2.00 | 0.040 | 0.017 | 0.75 | 16.0-18.0 | 10.0-14.0 | 2.00-3.00 | 0.10 | 0.50 |
MECHANICAL PROPERTIES ASTM A269
| SS | O.D. | W.T. | Yield strength | Tensile Strength | Elongation | Hardness |
| Inch | Inch | Psi | Psi | % | HV | |
| Min | Min | Min | Max | |||
| 316L | 1/8 | 0.022 | 30,000 | 75,000 | 35 | 200 |
| 316L | 1/8 | 0.028 | 30,000 | 75,000 | 35 | 200 |
| 316L | 1/8 | 0.035 | 30,000 | 75,000 | 35 | 200 |
| 316L | 1/4 | 0.035 | 30,000 | 75,000 | 35 | 200 |
| 316L | 1/4 | 0.049 | 30,000 | 75,000 | 35 | 200 |
| 316L | 1/4 | 0.065 | 30,000 | 75,000 | 35 | 200 |
| 316L | 3/8 | 0.035 | 30,000 | 75,000 | 35 | 200 |
| 316L | 3/8 | 0.049 | 30,000 | 75,000 | 35 | 200 |
| 316L | 3/8 | 0.065 | 30,000 | 75,000 | 35 | 200 |
| 316L | 3/8 | 0.083 | 30,000 | 75,000 | 35 | 200 |
| 316L | 1/2 | 0.035 | 30,000 | 75,000 | 35 | 200 |
| 316L | 1/2 | 0.049 | 30,000 | 75,000 | 35 | 200 |
| 316L | 1/2 | 0.065 | 30,000 | 75,000 | 35 | 200 |
| 316L | 1/2 | 0.083 | 30,000 | 75,000 | 35 | 200 |
| 316L | 5/8 | 0.028 | 30,000 | 75,000 | 35 | 200 |
| 316L | 5/8 | 0.035 | 30,000 | 75,000 | 35 | 200 |
| 316L | 5/8 | 0.049 | 30,000 | 75,000 | 35 | 200 |
| 316L | 5/8 | 0.083 | 30,000 | 75,000 | 35 | 200 |